Polyimides rank among the most heat-resistant polymers and find application in a variety of fields, including transportation, electronics, and membrane technology. The aim of this work is to study the structural, thermal, mechanical, and gas permeation properties of polyimide based nanocomposite membranes in flat sheet configuration. For this purpose, numerous advanced techniques such as atomic force microscopy (AFM), SEM, TEM, TGA, FT-IR, tensile strength, elongation test, and gas permeability measurements were carried out. In particular, BTDA–TDI/MDI (P84) co-polyimide was used as the matrix of the studied membranes, whereas multi-wall carbon nanotubes were employed as filler material at concentrations of up to 5 wt.% All studied films were prepared by the dry-cast process resulting in non-porous films of about 30–50 μm of thickness. An optimum filler concentration of 2 wt.% was estimated. At this concentration, both thermal and mechanical properties of the prepared membranes were improved, and the highest gas permeability values were also obtained. Finally, gas permeability experiments were carried out at 25, 50, and 100 ◦C with seven different pure gases. The results revealed that the uniform carbon nanotubes dispersion lead to enhanced gas permeation properties.
The main scope of this work is to develop nano-carbon-based mixed matrix celluloseacetate membranes (MMMs) for the potential use in both gas and liquid separation processes. Forthis purpose, a variety of mixed matrix membranes, consisting of cellulose acetate (CA) polymerand carbon nanotubes as additive material were prepared, characterized, and tested. Multi-walledcarbon nanotubes (MWCNTs) were used as filler material and diacetone alcohol (DAA) as solvent.The first main objective towards highly efficient composite membranes was the proper preparationof agglomerate-free MWCNTs dispersions. Rotor-stator system (RS) and ultrasonic sonotrode (USS)were used to achieve the nanofillers’ dispersion. In addition, the first results of the application of thethree-roll mill (TRM) technology in the filler dispersion achieved were promising. The filler material,MWCNTs, was characterized by scanning electron microscopy (SEM) and liquid nitrogen (LN2)adsorption-desorption isotherms at 77 K. The derivatives CA-based mixed matrix membranes werecharacterized by tensile strength and water contact angle measurements, impedance spectroscopy,gas permeability/selectivity measurements, and water permeability tests. The studied membranesprovide remarkable water permeation properties, 12–109 L/m2/h/bar, and also good separationfactors of carbon dioxide and helium separations. Specifically, a separation factor of 87 for 10%He/N2feed concentration and a selectivity value of 55.4 for 10% CO2/CH4feed concentrationwere achieved.