One-step preparation of bilayered films from kraft lignin and cellulose acetate to mimic tree bark
(2020)
This contribution presents the development of a dry-cast method for the one-step preparation of bio-based films from wood polymers that mimic the bilayered structure of tree bark, the natural protective layer of the tree. In a simplified view, natural bark can be considered as the superposition of an external homogeneous and non-porous layer (outer bark) and a porous substructure layer (inner bark). This work is a first step for the future development of bio-based biomimetic wood coatings. The film had a bark-like appearance and its total density, bulk density and porosity were similar to values measured in natural bark. Furthermore, the structural characteristics of the studied film, namely specific surface area (BET) and pore size distribution, as well as the performance of the water adsorption ability were investigated and discussed.
Porous polymer membranes substantially contribute to an acceleration of sustainability transformation based on the energy efficient separation of liquid and gaseous mixtures. This rapid shift toward sustainable industrial processes leads to an increased demand for specifically tailored membranes. In order to predict membrane performance factors like permeability, selectivity and durability, the membrane formation process by film casting and phase inversion needs to be understood further. In recent years, computational models of the membrane formation process have been studied intensely. Their high spatial and temporal resolution allows a detailed quantitative description of phase inversion phenomena. New experimental techniques complement this development, as they provide quantitative data, e.g., on compositional changes of the polymer solution during membrane formation as well as the kinetic progression of the phase separation process. This state-of-the-art review compiles computational and experimental approaches that characterize the phase inversion process. We discuss how this methodological pluralism is necessary for improving the tailoring of membrane parameters, but that it is unlikely to be the way to the ultimate goal of a complete description of the evolution of the membrane structure from the initial demixing to the final solidification. Alternatively, we formulate an approach that includes a database of standardized and harmonized membrane performance data based on previously publicized data, as well as the application of artificial neural networks as a new powerful tool to link membrane production parameters to membrane performance.
Polyimides rank among the most heat-resistant polymers and find application in a variety of fields, including transportation, electronics, and membrane technology. The aim of this work is to study the structural, thermal, mechanical, and gas permeation properties of polyimide based nanocomposite membranes in flat sheet configuration. For this purpose, numerous advanced techniques such as atomic force microscopy (AFM), SEM, TEM, TGA, FT-IR, tensile strength, elongation test, and gas permeability measurements were carried out. In particular, BTDA–TDI/MDI (P84) co-polyimide was used as the matrix of the studied membranes, whereas multi-wall carbon nanotubes were employed as filler material at concentrations of up to 5 wt.% All studied films were prepared by the dry-cast process resulting in non-porous films of about 30–50 μm of thickness. An optimum filler concentration of 2 wt.% was estimated. At this concentration, both thermal and mechanical properties of the prepared membranes were improved, and the highest gas permeability values were also obtained. Finally, gas permeability experiments were carried out at 25, 50, and 100 ◦C with seven different pure gases. The results revealed that the uniform carbon nanotubes dispersion lead to enhanced gas permeation properties.
The main scope of this work is to develop nano-carbon-based mixed matrix celluloseacetate membranes (MMMs) for the potential use in both gas and liquid separation processes. Forthis purpose, a variety of mixed matrix membranes, consisting of cellulose acetate (CA) polymerand carbon nanotubes as additive material were prepared, characterized, and tested. Multi-walledcarbon nanotubes (MWCNTs) were used as filler material and diacetone alcohol (DAA) as solvent.The first main objective towards highly efficient composite membranes was the proper preparationof agglomerate-free MWCNTs dispersions. Rotor-stator system (RS) and ultrasonic sonotrode (USS)were used to achieve the nanofillers’ dispersion. In addition, the first results of the application of thethree-roll mill (TRM) technology in the filler dispersion achieved were promising. The filler material,MWCNTs, was characterized by scanning electron microscopy (SEM) and liquid nitrogen (LN2)adsorption-desorption isotherms at 77 K. The derivatives CA-based mixed matrix membranes werecharacterized by tensile strength and water contact angle measurements, impedance spectroscopy,gas permeability/selectivity measurements, and water permeability tests. The studied membranesprovide remarkable water permeation properties, 12–109 L/m2/h/bar, and also good separationfactors of carbon dioxide and helium separations. Specifically, a separation factor of 87 for 10%He/N2feed concentration and a selectivity value of 55.4 for 10% CO2/CH4feed concentrationwere achieved.